A3B_oP32_62_ab4c_2c & a,b/a,c/a,x3,z3,x4,z4,x5,z5,x6,z6,x7,z7,x8,z8 --params=7.57,0.969749009247,1.02430647292,0.231,0.473,0.222,0.029,0.496,0.238,0.485,0.724,0.471,0.469,0.47,-0.032 & Pnma D_{2h}^{16} #62 (abc^6) & oP32 & None & O3W & O3W & P. M. Woodward and A. W. Sleight and T. Vogt, J. Solid State Chem. 131, 9-17 (1997) 1.00000000000000 7.57000000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.34100000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.75400000000000 O W 24 8 Direct 0.00000000000000 0.00000000000000 0.00000000000000 O (4a) 0.50000000000000 0.00000000000000 0.50000000000000 O (4a) 0.00000000000000 0.50000000000000 0.00000000000000 O (4a) 0.50000000000000 0.50000000000000 0.50000000000000 O (4a) 0.00000000000000 0.00000000000000 0.50000000000000 O (4b) 0.50000000000000 0.00000000000000 0.00000000000000 O (4b) 0.00000000000000 0.50000000000000 0.50000000000000 O (4b) 0.50000000000000 0.50000000000000 0.00000000000000 O (4b) 0.23100000000000 0.25000000000000 0.47300000000000 O (4c) 0.26900000000000 0.75000000000000 0.97300000000000 O (4c) -0.23100000000000 0.75000000000000 -0.47300000000000 O (4c) 0.73100000000000 0.25000000000000 0.02700000000000 O (4c) 0.22200000000000 0.25000000000000 0.02900000000000 O (4c) 0.27800000000000 0.75000000000000 0.52900000000000 O (4c) -0.22200000000000 0.75000000000000 -0.02900000000000 O (4c) 0.72200000000000 0.25000000000000 0.47100000000000 O (4c) 0.49600000000000 0.25000000000000 0.23800000000000 O (4c) 0.00400000000000 0.75000000000000 0.73800000000000 O (4c) -0.49600000000000 0.75000000000000 -0.23800000000000 O (4c) 0.99600000000000 0.25000000000000 0.26200000000000 O (4c) 0.48500000000000 0.25000000000000 0.72400000000000 O (4c) 0.01500000000000 0.75000000000000 1.22400000000000 O (4c) -0.48500000000000 0.75000000000000 -0.72400000000000 O (4c) 0.98500000000000 0.25000000000000 -0.22400000000000 O (4c) 0.47100000000000 0.25000000000000 0.46900000000000 W (4c) 0.02900000000000 0.75000000000000 0.96900000000000 W (4c) -0.47100000000000 0.75000000000000 -0.46900000000000 W (4c) 0.97100000000000 0.25000000000000 0.03100000000000 W (4c) 0.47000000000000 0.25000000000000 -0.03200000000000 W (4c) 0.03000000000000 0.75000000000000 0.46800000000000 W (4c) -0.47000000000000 0.75000000000000 0.03200000000000 W (4c) 0.97000000000000 0.25000000000000 0.53200000000000 W (4c)